Low-carbon steels

Electrodes of ANO and MR-3 brands are
used for welding of structures from low-strength steels
and are intended for manual arc welding.
  • -10%
    • Diameter 3
    • Weight 1
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 90 грн100 грн
    • Diameter 3
    • Weight 1
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 3
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 207 грн230 грн
    • Diameter 3
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 405 грн450 грн
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 400 грн445 грн
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 2,0
    • Weight 1,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 130 грн144 грн
    • Diameter 2,0
    • Weight 1,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 3,0
    • Weight 1,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 117 грн130 грн
    • Diameter 3,0
    • Weight 1,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 3,0
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 270 грн300 грн
    • Diameter 3,0
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 3,0
    • Weight 5,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 495 грн550 грн
    • Diameter 3,0
    • Weight 5,0
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥78
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 270 грн300 грн
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥78
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 495 грн550 грн
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥420
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 396 грн440 грн
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 387 грн430 грн
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 5
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 387 грн430 грн
    • Diameter 5
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 3
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 410 грн455 грн
    • Diameter 3
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 405 грн450 грн
    • Diameter 4
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 5
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • 405 грн450 грн
    • Diameter 5
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥22
    • Impact strength, J / cm2 KCU, + 200 C ≥78
  • -10%
    • Diameter 3
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 198 грн220 грн
    • Diameter 3
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 396 грн440 грн
    • Diameter 3
    • Weight 5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 198 грн220 грн
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
  • -10%
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -
    • 387 грн430 грн
    • Diameter 4
    • Weight 2,5
    • Temporary resistance to rupture, MPa ≥450
    • Welded materials Steels up to a yield strength of 380 N/mm2 (55 ksi)
    • Yield strength, MPa ≥380
    • Relative elongation,% ≥18
    • Impact strength, J / cm2 KCU, + 200 C ≥78
    • Impact force, KCV, J, -400C -

The main features are: 

  • providing a well-formed weld 
  • prevention of porosity and cracking 
  • provide ease of ignition of the arc and its stability {{ 1}} - no problems with slag separation 

In general, the electrodes of the brand "ANO" are used for welding oversized metal structures of small thickness, as well as for installation, welding of irresponsible structures, for welding gas and water pipes 

Features of MR-3 electrodes are: 

  • ensuring high-quality and uninterrupted operation in conditions of high humidity 
  • welding of even oxidized metal and metal damaged by rust 
  • allow for long arc welding 
  • providing a highly reliable seam even when using household power sources 

Electrodes MR-3 are used for welding critical structures, welding pipelines for the passage of water.