Welding electrodes АNО-4 3 мм 5 kg

Code: 1809
Welding electrodes АNО-4 3 мм 5 kg
Code: 1809
In Stock
  • 440 грн
Quick Checkout
Pay in installments
73 hrn
x 6 month
6
6
Department of Nova Poshta
Courier Nova Poshta
According to the tariff Nova Poshta
Courier Paton
Free from UAH 3,000.
Free
Specification
Diameter 3
Weight 5
Temporary resistance to rupture, MPa ≥450
Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
Yield strength, MPa ≥380
Relative elongation,% ≥22
Impact strength, J / cm2 KCU, + 200 C ≥78
Impact force, KCV, J, -400C -
Show all specifications
Description
The electrodes are designed for welding structures of low-carbon steel grades with a carbon content of not more than 0.25% in all spatial positions, except vertical top-down, metal with a thickness of 3 to 20 mm.
The electrodes are characterized by easy ignition, stable arc combustion, no defects in the welding process at high modes, as well as a low tendency to form pores in the root seams of T-joints. Welding of wet, rusty and poorly cleaned of oxides and other contaminants of metal is allowed.

Chemical composition of the weld metal:

Content of elements,%

С

≤0,10

Si

0,15–0,40

Mn

0,40–0,75

P

≤0,035

S

≤0,035



Classification:

Сertificates:

EN ISO 2560-A: E 38 0 RC 12                                      

AWS A5.1: E 6013

GOST 9466: E46-AHO-4-d-UD

                           E432 (3) -P31

Paton CERT

UkrSEPRO

ABS

СЄ


                

Welding current, welding position:

АС/DC +/-

C:\Users\USER10\AppData\Local\Microsoft\Windows\INetCache\Content.Outlook\0LOV6DM8\el.jpg

The electrodes are designed for welding structures of low-carbon steel grades with a carbon content of not more than 0.25% in all spatial positions, except vertical top-down, metal with a thickness of 3 to 20 mm.
The electrodes are characterized by easy ignition, stable arc combustion, no defects in the welding process at high modes, as well as a low tendency to form pores in the root seams of T-joints. Welding of wet, rusty and poorly cleaned of oxides and other contaminants of metal is allowed.

Chemical composition of the weld metal:

Content of elements,%

С

≤0,10

Si

0,15–0,40

Mn

0,40–0,75

P

≤0,035

S

≤0,035



Classification:

Сertificates:

EN ISO 2560-A: E 38 0 RC 12                                      

AWS A5.1: E 6013

GOST 9466: E46-AHO-4-d-UD

                           E432 (3) -P31

Paton CERT

UkrSEPRO

ABS

СЄ


                

Welding current, welding position:

АС/DC +/-

C:\Users\USER10\AppData\Local\Microsoft\Windows\INetCache\Content.Outlook\0LOV6DM8\el.jpg

" />
Complete set
  • Welding electrodes АNО-4  3 мм 5 kg
Testimonials
Leave a review
Specification
Diameter 3
Weight 5
Temporary resistance to rupture, MPa ≥450
Welded materials Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi)
Yield strength, MPa ≥380
Relative elongation,% ≥22
Impact strength, J / cm2 KCU, + 200 C ≥78
Impact force, KCV, J, -400C -