| Diameter | 5 |
| Weight | 5 |
| Temporary resistance to rupture, MPa | ≥450 |
| Welded materials | Steels up to a yield strength of 380 N/mm2 (55 ksi) |
| Yield strength, MPa | ≥380 |
| Relative elongation,% | ≥22 |
| Impact strength, J / cm2 KCU, + 200 C | ≥78 |
Electrodes are intended for welding of designs from low-carbon grades of steels in accordance with DSTU 2651 / GOST 380 (St0 and St1, St2, St3, all degrees of deoxidation "KP", "PS", "SP") and GOST 1050 (05kp, 08kp, 08ps, 08 , 10kp, 10ps, 10, 15kp, 15ps, 15, 20kp, 20ps, 20).
Welding can be performed in all spatial positions, except vertical top-down, direct or alternating current. The electrodes are characterized by a lack of tendency to form pores, which are caused by rust on the edges of parts or moistening of the coating and increased productivity of the welding process.
Chemical composition of the weld metal:
Electrodes are intended for welding of designs from low-carbon grades of steels in accordance with DSTU 2651 / GOST 380 (St0 and St1, St2, St3, all degrees of deoxidation "KP", "PS", "SP") and GOST 1050 (05kp, 08kp, 08ps, 08 , 10kp, 10ps, 10, 15kp, 15ps, 15, 20kp, 20ps, 20).
Welding can be performed in all spatial positions, except vertical top-down, direct or alternating current. The electrodes are characterized by a lack of tendency to form pores, which are caused by rust on the edges of parts or moistening of the coating and increased productivity of the welding process.
Chemical composition of the weld metal:
- Welding electrodes МР-3 5 мм 5 kg
| Diameter | 5 |
| Weight | 5 |
| Temporary resistance to rupture, MPa | ≥450 |
| Welded materials | Steels up to a yield strength of 380 N/mm2 (55 ksi) |
| Yield strength, MPa | ≥380 |
| Relative elongation,% | ≥22 |
| Impact strength, J / cm2 KCU, + 200 C | ≥78 |