| Diameter | 4 |
| Weight | 5 |
| Temporary resistance to rupture, MPa | ≥450 |
| Welded materials | Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi) |
| Yield strength, MPa | ≥380 |
| Relative elongation,% | ≥22 |
| Impact strength, J / cm2 KCU, + 200 C | ≥78 |
| Impact force, KCV, J, -400C | - |
The electrodes are designed for welding structures of low-carbon steel grades with a carbon content of not more than 0.25% in all spatial positions, except vertical top-down, metal with a thickness of 3 to 20 mm.
The electrodes are characterized by easy ignition, stable arc combustion, no defects in the welding process at high modes, as well as a low tendency to form pores in the root seams of T-joints. Welding of wet, rusty and poorly cleaned of oxides and other contaminants of metal is allowed.
Chemical composition of the weld metal:
The electrodes are designed for welding structures of low-carbon steel grades with a carbon content of not more than 0.25% in all spatial positions, except vertical top-down, metal with a thickness of 3 to 20 mm.
The electrodes are characterized by easy ignition, stable arc combustion, no defects in the welding process at high modes, as well as a low tendency to form pores in the root seams of T-joints. Welding of wet, rusty and poorly cleaned of oxides and other contaminants of metal is allowed.
Chemical composition of the weld metal:
- Welding electrodes АNО-4 4 мм 5 kg
| Diameter | 4 |
| Weight | 5 |
| Temporary resistance to rupture, MPa | ≥450 |
| Welded materials | Конструкційні сталі з межею текучості до 380 N/mm2 (55 ksi) |
| Yield strength, MPa | ≥380 |
| Relative elongation,% | ≥22 |
| Impact strength, J / cm2 KCU, + 200 C | ≥78 |
| Impact force, KCV, J, -400C | - |