CLASSIC MR-3
CLASSIC MP-3 diameter 3mm, weight packs 5kg
CLASSIC MP-3 diameter 3mm, weight packs 5kg
CLASSIC MP-3 diameter 4mm, weight packs 5kg
CLASSIC MP-3 diameter 5mm, weight packs 5kg
Price on request
Price on request
Price on request

Type of coating: rutile.
Э46-MP-3-d-УД
Е430(3)-Р26
Certified in UkrSEPRO

ГОСТ 9466-75; Э 46 по ГОСТ 9467
Е43 2 R26 по ISO 2560
E38 2 R 12 поEN 499
E6012 по AWS A5.1
ТУУ 054169 23.050-99

They are designed for welding of carbon steel structures with a carbon content of not more than 0.25%. They are characterized by the good formation of the weld metal and provide high resistance of the weld metal against the formation of porosity and hot cracks. It is possible formation of pores in the weld when welding at elevated conditions.

ХИМИЧЕСКИЙ СОСТАВ МЕТАЛЛА,%

СSiMnSP
≤ 0.10≤ 0.200.50-0.80≤ 0.040≤ 0.045

МЕХАНИЧЕСКИЕ СВОЙСТВА МЕТАЛЛА ШВА

Временное сопротивление разрыву, Н/мм²Относительное удлинение, %Ударная вязкость, Дж/см²KCV>34 Дж/см² При температуре, °С
≥450≥18≥78-20

РАЗМЕРЫ, СВАРОЧНЫЙ ТОК

Диаметр, ммДлина, ммДиапазон сварочного тока, мм, АСреднее количество электродов, мм, шт
3,035080-14039
4,0450140-22016
5,0450160-26011
6,0450270-320 

ХАРАКТЕРИСТИКИ РАСПЛАВЛЕНИЯ

Выход направленного металла, %Расход электродов на 1 кг наплавленного металла, кгКоэфициэнт наплавки, г(А час)
901,78,0-8,5

Режим повторного прокаливания: (170±10)°С/40 мин.